THREEBOND 1303B
- Brand: ???ThreeBond
- Type: ???TB1303B
ThreeBond 1300 Series (anaerobic strength sealant)
ThreeBond 1300 series products are made of the proprietary R & D strength anaerobic sealant. It is an ordinary sealants, adhesives difference is that once exposed to air, can not be fixed, to fill the tiny gap in the metal and separate air conditions at room temperature to complete the hardening process. Very anti-vibration hardened, heat resistance, resistance, etc., be able to machinery, plant parts such as screws and chimeric way through the combination of chemical reaction, and to effectively prevent loosening or leaking. This product is a one component solvent-free operation easy.
Click the product number to display its characteristics. For some products, links to details on the product page.
Product name Appearance viscosity torques curing speed can use lubricating the temperature range
mPa · s (cP) N.m (kgf · cm) to the practical strength
Time until the strongest intensity
Time until
℃
General
Link
Screw
Wire
With 1303N
Green 150 (150) 45 (460) ~ 1 hour to 12 hours
-40 ~ 150
1324N
Red 600 (600) 26 (270) ~ 1 hour to 12 hours ○ -40 ~ 150
1344N
Blue 600 (600) 16 (160) ~ 1 hour to 12 hours ○ -40 ~ 150
1360E
Blue 200 (200) 43 hours ~ 12 hours ~ 2 -40 ~ 200
1360F
Green 500 (500) 42 hours ~ 12 hours ~ 1 -40 ~ 200
1386D red bean color 1800 (1800) (160) ~ 1 hour to 12 hours ○ -40 ~ 150
Strength of the appearance of the viscosity of the chimeric product name
(Fe) mosaic intensity
(Stainless steel) chimeric strength
(Al) solidification time UV-curing
mPa · s (cP) MPa (kgf · cm) MPa (kgf · cm) MPa (kgf · cm) min
Inlay
Co
With the 1359D
Blue 14000 (14000) 32 (326) 20 (203) 18 (188) 2 ○
1372D
Green 110 (110) 33 (336) 31 (311) 27 (275) 3 ○
1373N
Green 90 (90) 38 (390) 31 (316) 36 (370) 2 ○
Appearance of the proportion of trade name products form volatile solvent composition drying time coagulation time ※ 1
End
Layer
Spread
Material
1390E light brown glass bottle of ethanol of about 0.8 for about 20 seconds 60 seconds
1390F 0.8 ** light brown glass bottles for about 10 seconds about 10 seconds
※ 1 PPS board, the primer coating in the vertical plane, the surface drying time of 25 ℃